Polydimethylsiloxane Membranes Containing Multi-walled Carbon Nanotubes for Gas Separation

Mixed matrix membranes were characterized by scanning electron microscopy, thermogravimetric analysis, Fourier transformed infrared, positron annihilation lifetime and Raman spectroscopies and X-ray diffraction. The permeabilities to CO2, CH4, N2 and O2 were determined.

No phase separation was noticed. For carbon nanotubes content of 1 wt%, it was shown a decrease in membrane permeability with slight increase in ideal selectivity, compared to pure PDMS. However, the increase in the filler load up to 6.7 wt% increased the free volume average size of the membranes, improving the contribution of the diffusion to the transport and decreasing ideal selectivities of CO2/CH4, CO2/N2 and O2/N2.