Bioethanol steam reforming for hydrogen production over Ni‑Cr/SBA 15: Influence of metal loading and Ni/Cr ratio

The characterization of the synthesized samples reveals that higher Cr amounts results in lower Ni crystallite sizes due to the promoting effect of Cr, thereby enhancing the dispersion of the active phase. The catalytic performance has been evaluated in terms of ethanol conversion and H2 TOF (min-1).

Ethanol conversion exhibits an increasing trend with higher Ni content, reaching up to 90% for samples containing 15 wt.%. By increasing the Cr content (lower Ni/Cr ratio) the results evidence a similar trend. A synergistic effect between Ni and Cr was appreciated in conversion values when the Ni content was below 11 wt.% and the Cr content exceeded 2 wt.%, which coincides with smaller Ni crystallite size.