Data for (M,Ru)O2 (M = Mg, Zn, Cu, Ni, Co) rutiles and their use as oxygen evolution electrocatalysts in membrane electrode assemblies under acidic conditions

The polycrystalline powders consist of lath-shaped crystallites, tens of nanometres in maximum dimension. Powder neutron diffraction shows that the materials have expanded a axis and contracted c axis compared to the parent RuO2, but there is no evidence of lowering of symmetry to other AO2-type structures, supported by Raman spectroscopy.

Rietveld refinement shows no evidence for oxide non-stoichiometry and provides a formula (MxRu1-x)O2 with 0.14 < x < 0.2, depending on the substituent metal. This is supported by energy-dispersive X-ray analysis on the transmission electron microscope, while Ru K-edge XANES spectroscopy shows that upon inclusion of the substituent the average Ru oxidation state is increased to balance charge. Variable temperature magnetic measurements provide evidence for atomic homogeneity of the mixed metal materials, with suppression of the high temperature antiferromagnetism of RuO2 and increased magnetic moment.