Characterization of ZnAl2O4 Spinel Obtained by Hydrothermal and Microwave Assisted Combustion Method: A Comparative Study

The materials were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and N2-adsorption/desorption isotherms. The XRD patterns confirmed the formation of cubic ZnAl2O4 spinel structure with no secondary phases for both synthesis routes, whereas the hydrothermal method yielded powders with crystallite size 3 times smaller (6.9 nm), as compared to the powders produced by microwave assisted combustion method (25.6 nm).

The micrographs revealed agglomerated powders with plate-like morphologies for both routes. Nitrogen adsorption/desorption isotherms (BET) revealed higher surface area (183 m2.g-1) and greater pore volume (0.173 cm3.g-1) for ZnAl2O4 powders prepared by the hydrothermal method.