A Functionally Graded PICN Material for Biomimetic CAD-CAM Blocks

Katana translucent zirconia (HT-ZIR) and e.max-CAD (EMX) were tested for comparison. Flexural strength, flexural load energy, and Weibull modulus of FG-PICN were shown to increase from the first (enamel-like zone) to the ninth layer (dentin-like zone), while, on the contrary, flexural modulus, hardness, brittleness index, and ceramic volume percentage decreased. SEM characterization highlighted a higher porosity in layer 9 than in layer 1.

Flexural strength of the dentin-like zone (372.7 ± 27.8 MPa) was similar to EMX and lower than HT-ZIR. Flexural modulus was shown to vary from 41.9 ± 5.1 to 28.6 ± 2.0 GPa from surface to depth. Flexural load energy in the dentin-like zone (27.1 ± 4.9 mJ) was significantly superior to EMX and HT-ZIR.

Hardness gradient was shown to be close to tooth tissues. This work introduces FG-PICN blocks, with a gradient of mechanical and optical properties through the entire thickness of the block designed to mimic dental tissues. FG-PICN demonstrated a favorable gradient of flexural strength, elastic modulus, and, most of all, flexural load energy and hardness compared to other CAD-CAM materials, which can promote the biomechanical behavior of single-unit restorations on teeth and implants.